ZXET Archives - MHXCo Foam Company

Density	12 pcf (192 kg/m³), 3 pcf (64 kg/m³), 5 pcf (96 kg/m³)
Thickness Range	.020–.100 in (0.5-2.5 mm), .024–.125 in (0.6-3.2 mm), .040–.188 in (1.0-4.8 mm)
Tensile Strength - Lengthwise	190 psi (1310 kPa), 450 psi (3100 kPa), 90 psi (620 kPa)
Tensile Strength - Crosswise	140 psi (965 kPa), 350 psi (2415 kPa), 68 psi (468 kPa)
Elongation - Lengthwise	331%, 340%, 390%
Elongation - Crosswise	300%, 302%, 360%
25% Compression Resistance	24 psi (165 kPa), 6 psi (41 kPa), 8 psi (55.2 kPa)
50% Compression Resistance	15 psi (103 kPa), 19 psi (131 kPa), 51 psi (350 kPa)
Compression Set	<10%, <20%
Tear Resistance - Lengthwise	16 pli (2.8 kN/m), 32 pli (5.8 kN/m), 66 pli (11.6 kN/m)
Tear Resistance - Crosswise	14 pli (2.4 kN/m), 21 pli (3.7 kN/m), 53 pli (9.3 kN/m)
Temperature Range	-110° — 180° F (-79° — 82° C)

Density

12 pcf (192 kg/m³), 3 pcf (64 kg/m³), 5 pcf (96 kg/m³)

Thickness Range

.020–.100 in (0.5-2.5 mm), .024–.125 in (0.6-3.2 mm), .040–.188 in (1.0-4.8 mm)

Tensile Strength - Lengthwise

190 psi (1310 kPa), 450 psi (3100 kPa), 90 psi (620 kPa)

Tensile Strength - Crosswise

140 psi (965 kPa), 350 psi (2415 kPa), 68 psi (468 kPa)

Elongation - Lengthwise

331%, 340%, 390%

Elongation - Crosswise

300%, 302%, 360%

25% Compression Resistance

24 psi (165 kPa), 6 psi (41 kPa), 8 psi (55.2 kPa)

50% Compression Resistance

15 psi (103 kPa), 19 psi (131 kPa), 51 psi (350 kPa)

Compression Set

<10%, <20%

Tear Resistance - Lengthwise

16 pli (2.8 kN/m), 32 pli (5.8 kN/m), 66 pli (11.6 kN/m)

Tear Resistance - Crosswise

14 pli (2.4 kN/m), 21 pli (3.7 kN/m), 53 pli (9.3 kN/m)

Temperature Range

-110° — 180° F (-79° — 82° C)

ZXET